Nanocrystalline composites in TiO2 and SnO2 system for ammonia resistance sensors
PBN-AR
Instytucja
Instytut Metalurgii i Inżynierii Materiałowej im. Aleksandra Krupkowskiego Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Processing and Application of Ceramics (30pkt w roku publikacji)
ISSN
1820-6131
EISSN
Wydawca
Faculty of Technology, University of Novi Sad
DOI
URL
Rok publikacji
2018
Numer zeszytu
3
Strony od-do
241-248
Numer tomu
12
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.50
Autorzy
(liczba autorów: 3)
Pozostali autorzy
+ 2
Streszczenia
Język
en
Treść
This work describes the production of nanocrystalline TiO2 and SnO2 oxides, as well as their nanocomposites (containing 26.9, 58.7 and 79.0 wt.% of SnO2) with two-stage sol-gel method combined with high temperature treatment. The phase composition and medium size crystallites were determined using X-ray diffraction analysis (XRD) and revealed that the nanocomposites crystallize in tetragonal structures of TiO2-anatase and SnO2-cassiterite. Specific surface area of the nanopowders, measured using sorption method (BET), changed from 42.1 to 160.8 m²/g. The morphology of the nanopowders was observed using transmission electron microscope (TEM). As indicated by TEM images, the manufactured nanopowders were well crystallized and consisted of small, spherical grains. The obtained nanopowders were also tested for NH3 gas detection application. The presented method of nanopowders synthesis enables to obtain nanocrystalline TiO2 and SnO2 oxides, as well as composites from TiO2-SnO2 of known and controlled chemical and phase composition. It also enables to obtain composites used for gas sensors. The sensor made of composite containing 58.7 wt.% of SnO2 exhibited the best NH3 sensing features. © 2018 University of Novi Sad Faculty of Technology. All rights reserved.
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:901849
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych