Design and assembly of ternary Pt/Re/SnO2 NPs by controlling the zeta potential of individual Pt, Re, and SnO2 NPs
PBN-AR
Instytucja
Instytut Fizyki Jądrowej im. Henryka Niewodniczańskiego Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
JOURNAL OF NANOPARTICLE RESEARCH (30pkt w roku publikacji)
ISSN
1388-0764
EISSN
Wydawca
DOI
URL
Rok publikacji
2018
Numer zeszytu
5
Strony od-do
144
Numer tomu
20
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
Catalytic nanoparticles
TEM characterization
Zeta potential
Pt
Re
SnO2 NPs
Nanocolloids
Open access
Tryb otwartego dostępu
Inne
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa
Czas opublikowania w otwartym dostępie
Razem z publikacją
Streszczenia
Język
en
Treść
In this study Pt, Re, and SnO2 nanoparticles (NPs) were combined in a controlled manner into binary and ternary combinations for a possible application for ethanol oxidation. For this purpose, zeta potentials as a function of the pH of the individual NPs solutions were measured. In order to successfully combine the NPs into Pt/SnO2 and Re/SnO2 NPs, the solutions were mixed together at a pH guaranteeing opposite zeta potentials of the metal and oxide NPs. The individually synthesized NPs and their binary/ternary combinations were characterized by Fourier transform infrared spectroscopy (FTIR) and scanning transmission electron microscopy (STEM) combined with energy dispersive X-ray spectroscopy (EDS) analysis. FTIR and XPS spectroscopy showed that the individually synthesized Pt and Re NPs are metallic and the Sn component was oxidized to SnO2. STEM showed that all NPs are well crystallized and the sizes of the Pt. Re, and SnO2 NPs were 2.2, 1.0, and 3.4 nm, respectively. Moreover, EDS analysis confirmed the successful formation of binary Pt/SnO2 and Re/SnO2 NP, as well as ternary Pt/Re/ SnO2 NP combinations. This study shows that by controlling the zeta potential of individual metal and oxide NPs, it is possible to assemble them into binary and ternary combinations.
Cechy publikacji
peer-reviewed
original-article
Inne
System-identifier
30223/2018
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych