Effect of 0.25 and 2.0 MeV $He-Ion$ irradiation on short-range ordering in model (EFDA) $Fe-Cr$ alloys
PBN-AR
Instytucja
Akademickie Centrum Materiałów i Nanotechnologii (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science (35pkt w roku publikacji)
ISSN
1073-5623
EISSN
1543-1940
Wydawca
Springer
DOI
Rok publikacji
2018
Numer zeszytu
8
Strony od-do
3729--3737
Numer tomu
49
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.64
Autorzy
(liczba autorów: 3)
Pozostali autorzy
+ 2
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa
Czas opublikowania w otwartym dostępie
Razem z publikacją
Streszczenia
Język
EN
Treść
The effects of He+ irradiation on a distribution of Cr atoms in Fe100−xCrx (x = 5.8, 10.75, 15.15) alloys were studied by 57Fe Conversion Electron Mössbauer Spectroscopy (CEMS). The alloys were irradiated with doses up to 12 × 1016 ions/cm2 with 0.25 and 2.0 MeV He+ ions. The distribution of Cr atoms within the first two coordination shells around Fe atoms was expressed with short-range order parameters α1 (first-neighbor shell, 1NN), α2 (second-neighbor shell, 2NN), and α12 (1NN + 2NN). In non-irradiated alloys, α1 >0 and α2 <0 was revealed for all three samples. The value of α12 ≈0, i.e., the distribution of Cr atoms averaged over 1NN and 2NN, was random. The effect of the irradiation of the Fe94.2Cr5.8 alloy was similar for the two energies of He+, viz., increase of number of Cr atoms in 1NN and decrease in 2NN. Consequently, the degree of ordering increased. For the other two samples, the effect of the irradiation depends on the composition, and is stronger for the less energetic ions where, for Fe89.25Cr10.75 alloy, the disordering disappeared and some traces of Cr clustering appeared. In Fe84.85Cr15.15 alloy, the clustering was clear. In the samples irradiated with 2. 0 MeV He+ ions, the ordering also survived in the samples with x = 10.75 and 15.15, yet its degree became smaller than in the Fe94.2Cr5.8 alloy.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:115149
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych