Structure and properties of composite layers of nitrided layers with surface zone of manganese phosphate type produced on 32CDV13 steel
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Mechaniki Precyzyjnej
Informacje podstawowe
Główny język publikacji
angielski
Czasopismo
Inżynieria Materiałowa (13pkt w roku publikacji)
ISSN
0208-6247
EISSN
Wydawca
Wydawnictwo Czasopism i Książek Technicznych SIGMA-NOT Sp. z o.o.
DOI
Rok publikacji
2017
Numer zeszytu
5
Strony od-do
231-236
Numer tomu
219
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
angielski
32CDV13 (1.8522) steel
composite layers
hybrid technologies
glow discharge nitriding
chemical phosphating
manganese phosphate
wear resistance
polski
stal 32CDV13 (1.8522)
warstwy kompozytowe
technologie hybrydowe
azotowanie jarzeniowe
fosforanowanie chemiczne
fosforany manganu
Streszczenia
Język
angielski
Treść
Due to its high mechanical properties the 32CDV13 steel is widely used in the industry for the production of highly loaded parts of machines and equipment. The increase in the durability and the reliability of elements is currently being achieved by using conventional methods of surface treatments: carburizing processes, burnishing and surface hardening. Hybrid processes constitute an alternative to these solutions, leading to obtaining of composite layers. They combine two or more techniques during surface treatments, enabling the formation of surface layers with unique and complementary properties. This paper presents the structure (light microscopy, SEM) and the results of friction wear resistance (“ball on disc” method) of composite layers produced on heat treated 32CDV13 steel after it was (hardness 36 HRC) subjected to the hybrid process which combined the glow discharge nitriding process and phosphating method. The results show improvement of tribological properties, especially reduction of friction coefficient in comparison to nitrided layer.
Inne
System-identifier
PX-5a96b8efd5debc41d8f17b62
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych