Electrical transport in low-lead (1-x)BaTiO3–xPbMg1/3Nb2/3 O3 ceramics
PBN-AR
Instytucja
Instytut Metalurgii i Inżynierii Materiałowej im. Aleksandra Krupkowskiego Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Journal of Advanced Ceramics (30pkt w roku publikacji)
ISSN
2226-4108
EISSN
Wydawca
DOI
URL
Rok publikacji
2017
Numer zeszytu
3
Strony od-do
207-219
Numer tomu
6
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0,81
Autorzy
(liczba autorów: 8)
Pozostali autorzy
+ 7
Słowa kluczowe
en
BT–PMN ceramics
electric properties
Seebeck coefficient
Streszczenia
Język
en
Treść
Low-lead (1−x)BaTiO3–xPbMg1/3Nb2/3O3 ceramics (x = 0, 0.025, 0.05, 0.075, 0.1, and 0.15) were prepared by the conventional oxide mixed sintering process, and their optical band gap, Seebeck coefficient, ac (σ ac) and dc (σ dc) conductivities as a function of temperature were investigated for the first time. It was found that all samples have p-type conductivity. The low-frequency (20 Hz–2 MHz) ac conductivity obeys a power law σ ac~ω s , which is characteristic for disordered materials. The frequency exponent s is a decreasing function of temperature and tends to zero at high temperature. σ ac is proportional to ω 0.07–ω 0.31 in the low-frequency region and to ω 0.51–ω 0.98 in the high-temperature region. The temperature dependence of the dc conductivity showed a change in slope around the temperature at which the phase transition appeared. Both ac and dc conductivities showed a thermally activated character and possessed linear parts with different activation energies and some irregular changes. It was found that the hopping charge carriers dominate at low temperature and small polarons and oxygen vacancies dominate at higher temperature. (1−x)BaTiO3–xPbMg1/3Nb2/3O3 ceramics are expected to be promising new candidate for low-lead electronic materials.
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:854851
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych