Fabrication and properties of electrode material composed of ordered titania nanotubes and pEDOT:PSS
PBN-AR
Instytucja
Wydział Chemiczny (Politechnika Gdańska)
Informacje podstawowe
Główny język publikacji
ENG
Czasopismo
SOLID STATE IONICS
ISSN
0167-2738
EISSN
Wydawca
DOI
URL
Rok publikacji
2015
Numer zeszytu
Strony od-do
56-62
Numer tomu
271
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
ANODIZATION
CONDUCTING POLYMER
PEDOT:PSS
TITANIA NANOTUBES
Streszczenia
Język
Treść
We report on the two-stage preparation method of electrode material composed of titania nanotubes and poly(3,4-ethylenedioxythiopene):poly(2-styrenesulphonate) conductive polymer (pEDOT:PSS). Initially, titania nanotube arrays were produced by the anodization process of Ti substrate. Next, the polymer was potentiostatically deposited onto the thermally annealed nanotube arrays from the electrolyte containing monomer and counter ion. The obtained material was characterized by means of Raman spectroscopy, SEM and photoluminescence spectroscopy. On the basis of electrochemical studies, a radical decrease in the electrode material resistance after conductive polymer deposition was detected. The enhancement in registered current under UV–vis irradiation was almost 4 times higher for a composite with the highest amount of deposited pEDOT:PSS in comparison to pristine titania nanotube array film.
Inne
System-identifier
131536
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych