Densification of SHS obtained $Ti_{2}AlC$ active precursor powder by hot pressing method
PBN-AR
Instytucja
Wydział Inżynierii Materiałowej i Ceramiki (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Książka
Tytuł książki
Processing and properties of advanced ceramics and composites VII
Data publikacji
2015
ISBN
978-1-119-18387-7
Wydawca
John Wiley \& Sons, Inc.
Publikacja
Główny język publikacji
EN
Tytuł rozdziału
Densification of SHS obtained $Ti_{2}AlC$ active precursor powder by hot pressing method
Rok publikacji
2015
Strony (od-do)
205--212
Numer rozdziału
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.57
Hasło encyklopedyczne
Autorzy
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
nie
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
MS\&T'14
Nazwa konferencji
Materials Science \& Technology 2014 conference
Początek konferencji
2014-10-12
Koniec konferencji
2014-10-16
Lokalizacja konferencji
Pittsburgh
Kraj konferencji
US
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
Ti2AlC belongs to the interesting group of ternary materials called MAX phases which can be found in the Ti-Al-C-N system. Thanks to the heterodesmic chemical bonding these nanolaminate structured materials possess unique set of properties locating them between metals and ceramics. One of the best methods of obtaining these materials, namely Self-propagating High-temperature Synthesis (SHS) was applied for synthesis of Ti2AlC active precursor powders. As a result of synthesis of various substrates mixtures including elementary powders (Ti, Al, C) and intermetallic compounds (TiAl) which were set in stoichiometric proportions as well as with excess amount of particular reactants powders containing mostly Ti2AlC, Ti3AlC2 and TiC were obtained. Selected powders were hot pressed in various conditions and changes of phase compositions which allowed obtaining single phase dense product as well as changes in apparent density of obtained powders were observed and optimal sintering conditions of Ti2AlC SHS derived powders were established. Copyright © 2015 by the American Ceramic Society. All rights reserved.