Microstructure and texture evolution in the welded semi-austenitic PH steel after the heat treatment
PBN-AR
Instytucja
Wydział Inżynierii Metali i Informatyki Przemysłowej (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Acta Physica Polonica. A
ISSN
0587-4246
EISSN
1898-794X
Wydawca
Polska Akademia Nauk. Instytut Fizyki
DOI
Rok publikacji
2016
Numer zeszytu
4
Strony od-do
956--959
Numer tomu
130
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.28
Streszczenia
Język
EN
Treść
The aim of this study was to reveal the influence of the heat treatment after welding of 17-7PH (X7CrNiAl17-7) steel on the microstructure evolution and the texture of the welds. Microstructure investigation carried out by light microscopy and transmission electron microscopy showed that the austenite and delta ferrite coexist in as-welded condition. Annealing at the temperature range between 400 degrees C and 620 degrees C after welding causes small changes in the microstructure and the hardness of the welds increases. Heat treatment at 760 degrees C for 1 h resulted in the partial destabilization of the austenite. Aging after destabilization leads to tempering of the martensite: first the hardness increases and then decreases. The maximum hardness is observed when the ageing temperature reaches 510 degrees C. XRD studies confirmed the presence of the two phases: delta ferrite and austenite. Annealing at 400 degrees C/1 h and 550 degrees C/1 h results in changes of the intensities for individual peaks derived from austenite and ferrite. The calculated ratios of peak intensity were compared with the intensities of the reference sample. The differences in intensities suggested strong texture of the material.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:103571
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych