Monolithic Zn–Co–Ti based sorbents for hot syngas desulfurization
PBN-AR
Instytucja
Instytut Chemicznej Przeróbki Węgla
Informacje podstawowe
Główny język publikacji
en
Czasopismo
FUEL PROCESSING TECHNOLOGY
ISSN
0378-3820
EISSN
Wydawca
ELSEVIER SCIENCE BV
DOI
URL
Rok publikacji
2016
Numer zeszytu
Strony od-do
64-70
Numer tomu
144
Identyfikator DOI
Liczba arkuszy
1.00
Streszczenia
Język
en
Treść
Charge of monolithic Zn–Co–Ti–O based sorbent was manufactured using natural clay as a binder and tested in model hot syngas desulfurization. Fresh and regenerated sorbent was characterized by XRD, SEM–EDX, XPS, mercury porosimetry, and TPRH2. After four cycles of desulfurization (at 540 °C) and regeneration (540–650 °C), monoliths retained the mechanical integrity and their geometry did not change. Monolithic sorbent captured 5.3 g S/100 g in the first cycle and 13.8 g S/100 g in the last one. Concentration of H2S in the treated gas was lowered from 6000 ppmv to 3 ppmv and the H2S removal efficiency was min. 99.6%. Fresh sorbent contains Zn2Ti3O8 (dominant phase), TiO2 and SiO2, while in the regenerated one always occurs: TiO2 (dominant phase), ZnTiO3, Zn2Ti3O8; SiO2; Zn2SiO4 and ZnAl2O4. Reducibility and the amount of sulfates formed in the used sorbent depend on its position in the bed. After tests, small amounts of free ZnO are present on the surface of the used monoliths. During regeneration the zinc oxide (from Zn–Ti–O mixed oxides) reacts with Al2O3 or SiO2 (clay components), and forms compounds more resistant to deactivation, such as Zn2SiO4 and ZnAl2O4.
Cechy publikacji
discipline:Energetyka
discipline:Inżynieria materiałowa
discipline:Energetics
discipline:Materials science
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:772493
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych