Numerical and experimental failure analysis of rifle extractor
PBN-AR
Instytucja
Wydział Mechatroniki i Lotnictwa (Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego)
Informacje podstawowe
Główny język publikacji
angielski
Czasopismo
ENGINEERING FAILURE ANALYSIS
ISSN
1350-6307
EISSN
Wydawca
European Structural Integrity Society
DOI
Rok publikacji
2016
Numer zeszytu
Strony od-do
112-127
Numer tomu
62
Liczba arkuszy
Autorzy
Pozostali autorzy
+ 2
Słowa kluczowe
en
assault rifle,
numerical investigations,
failure analysis,
mechanical damage,
heat treatment
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Inna
Czas opublikowania w otwartym dostępie
Razem z publikacją
Streszczenia
Język
en
Treść
The purpose of this article is to present a research methodology used to determine the causes of mechanical damage of a cartridge case extractor in a newly designed 5.56 mm assault rifle. It combines numerical analyses and materials science research. Based on the results obtained through simulation studies utilizing the Finite Element Method, values of local stress concentrations in the case extractor were identified. The paper provides detailed information on the used numerical models and adopted initial-boundary conditions required to carry out computer simulations. Based on the obtained values of maximal principal stress, the authors decided to carry out additional experimental research in order to reveal the cause of extractor damage. An adopted approach was consisted of micro hardness and metallographic analysis of the images depicting the microstructure of the extractor material. There were not observed any negative effects of an extractor heat treatment process on mechanical properties of the extractor material. Additional metallographic tests revealed that the main reasons of extractor failures were structural defects of material used in the manufacturing process of the extractor.
Cechy publikacji
Review Article
Inne
System-identifier
PX-56bf6e4081062a841e96c7ee
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych